FEP PF4630

Get to know Everflon+™ FEP PF4630.

Everflon+™ FEP PF4630 is a fluoroplastic resin com-pounded with a foam nucle-ating package. This resin is supplied as white pellets and is used in a nitrogen gas-in-jected foam extrusion pro-cess to produce uniform foam cells in the dielectric insulation. Foaming the fluo-roplastic reduces its dielec-tric constant, providing op-portunities for miniaturiza-tion and weight savings. Foamed insulation of Ever-flon+™ FEP PF4630 produces cables for high frequency signal transmission with minimal distortion.

Everflon+™ FEP PF4630 is ideal for producing coaxial cable cores in a broad range of sizes. A typical coaxial cable core would have conductor sizes of 32 AWG or greater, wall thickness of 0.004 in or greater, with void content from 20% to 60%.

These voids are closed cell in nature and range from 0.018 mm ( 0.0007 in) to 0.127 mm in (0.005in) in diameter. Achievable void content will vary based on wall thick-ness and processing conditions.

Related Products

FEP PF4630
FEP PF4622
FEP PF4610

Data List

Tentative Typical Property Data for Everflon+™ FEP PF4630 Fluoropolymer Resin

Properties	Test Method&Unit	Typical Value
Melt Flow Rate at 372 °C (702 °F)/5.0 kg weight	ISO 12086/ASTM D2116 g/10 min	27~33
Melting Point	D4591 °C	260
Specific Gravity	D792	2.15
Tensile Strength	ISO 12086/ASTM D2116 MPa	18
Elongation at Break	ISO 12086/ASTM D2116 %	300
Dielectric Constant	ASTM D150 1 GHz	2.0
Dissipation Factor	ASTM D150 1 GHz	0.0004

Processing Guide

Everflon+™ PF FEP can be fed directly to a conventional singlescrew extruder with nitrogen gas injection. The process contact metals must be high-nickel, low-iron alloys suitable for fluoroplastic processing. The process should include devices to monitor diameter, capacitance, and gas flow.

When adding color concentrate, use one compounded in FEP fluoroplastic. Color addition may affect cell formation and capacitance, requiring process adjustment.

Insulation performance is determined by extruder output, wire line speed, and void content. Void content is controlled by nitrogen flow rate, process tem-peratures, and quench point. It is best for the voids to grow after the melt is drawn down onto the wire. Elongated voids in the insulation indicate early growth of the cells in the draw-down cone.

Precaution

Before using Everflon™ FEP resin, refer to the Safety Data Sheet and the latest edition of “The Guide to the Safe Handling of Fluoropolymer Resins”.

Open and use containers only in wellventilated areas using local exhaust ventilation (LEV). Vapors and fumes liberated during hot processing of Everflon™ FEP should be exhausted completely from the work area. Contamination of tobacco with these polymers must be avoided. Vapors and fumes liberated during hot processing that are not properly exhausted, or from smoking tobacco or cigarettes contaminated with Everflon™ FEP , may cause flulike symptoms, such as chills, fever, and sore throat. This may not occur until several hours after exposure and will typically pass within about 24 hours. Mixtures with some finely divided metals, such as magnesium or aluminum, can be flammable or explosive under some conditions.

Handing and Package

The properties of Everflon™ FEP resins are not affected by storage time. Ambient storage conditions should be designed to avoid airborne contamination and water condensation on the resin when it is removed from containers. Drying at 100 °C (212 °F) for 4 hours is suggested to remove any absorbed moisture.

Everflon™ FEP PF4630 is supplied as pellets and packaged in 25-kg drums with a polyethylene inner lining.